20+ Years OEM/ODM Experience
+86 152 2111 0591
🇫🇷

HVAC Industry Solutions

Blog de Distribución de Aire | Soluciones HVAC Personalizadas | HVACore

Latest Blog

Stay updated with the latest trends, innovations, and insights from the HVAC manufacturing industry.

Read More
Custom HVAC plastic components manufacturing banner
Compare PETG y ABS para piezas plásticas de HVAC: resistencia al calor, resistencia química, deformación, procesabilidad y costo. Elija la resina adecuada para carcasas, conductos y paneles.

Compare PETG y ABS para piezas plásticas de HVAC: resistencia al calor, resistencia química, alabeo, procesabilidad y costo. Elija la resina adecuada...

Compare PETG and ABS for HVAC plastic parts: heat resistance, chemical resistance, warpage, processability, and cost. Choose the right resin for housings, ducts, and panels.
Read More
Read More
Collection of gray plastic HVAC components including ducts, elbows, and connectors arranged on a neutral background.
Puntos clave Los plásticos tienen un coeficiente de pérdida 5–100 veces mayor que el acero y el aluminio, lo que significa que disipan la energía de vibración en forma de calor en lugar de amplificarla como sonido. El moldeo de dos inyecciones (2K) une nylon estructural rígido a capas de aislamiento TPE blandas en un solo ciclo, eliminando el traqueteo microscópico causado por las arandelas de goma separadas. Añadir 20–40% de carga de talco a […]

Colección de componentes de HVAC de plástico gris que incluyen conductos, codos y conectores dispuestos sobre un fondo neutro.

Key Takeaways Plastics have a loss coefficient 5–100x higher than steel and aluminum, meaning they dissipate vibration energy as heat instead of amplifying it as sound. Two-Shot (2K) molding bonds rigid structural nylon to soft TPE isolation layers in a single cycle, eliminating the micro-rattle caused by separate rubber grommets. Adding 20–40% talc filler to […]
Read More
Read More
Portable air conditioner with flexible exhaust hose installed in a window, next to a side table with a lamp and plant in a stylish room.
Puntos Clave Las carcasas de sensores HVAC inteligentes requieren tolerancias inferiores a 0,05 mm para evitar el agrietamiento de la pantalla táctil y la desintonización de la antena. Las mezclas de PC/ABS dominan las carcasas de termostatos inteligentes porque combinan una resistencia al impacto de 65 kJ/m2 con una temperatura de deflexión por calor de 110 grados Celsius. Los canales de refrigeración conformes reducen el tiempo de ciclo en un 25-35% y disminuyen la deformación hasta en un 60% […]

El diseño requería un ensamblaje por presión donde la placa frontal encajaba en la placa trasera montada en la pared. Durante la prueba T1, las placas traseras se combaron en el centro como un plátano (alabeo de 1.2mm). Al atornillarse a una pared de yeso, los mecanismos de presión se desplazaron de su posición y la placa frontal no lograba trabarse.

Key Takeaways Smart HVAC sensor housings require tolerances below 0.05 mm to prevent touchscreen cracking and antenna detuning. PC/ABS blends dominate smart thermostat housings because they combine 65 kJ/m2 impact strength with a heat deflection temperature of 110 degrees Celsius. Conformal cooling channels reduce cycle time by 25-35% and cut warpage by up to 60% […]
Read More
Read More
ASTM D792
Puntos Clave ABS ofrece mayor resistencia al calor (HDT 88–103 °C) frente a PETG (65–80 °C), lo que lo hace mejor para componentes cerca de fuentes de calor. PETG supera a ABS en resistencia química a ácidos, aceites y agentes de limpieza utilizados en mantenimiento HVAC. ABS tiene menor variación de contracción por moldeo y mejor estabilidad dimensional para carcasas HVAC de tolerancia ajustada. PETG es naturalmente […]

ASTM D792

Key Takeaways ABS offers higher heat resistance (HDT 88–103 °C) vs PETG (65–80 °C), making it better for components near heat sources. PETG outperforms ABS in chemical resistance to acids, oils, and cleaning agents used in HVAC maintenance. ABS has lower mold shrinkage variance and better dimensional stability for tight-tolerance HVAC housings. PETG is naturally […]
Read More
Read More
Puntos Clave El nailon con carga de vidrio (PA66-GF) reemplaza al metal en HVAC con un ahorro de peso del 30–40% manteniendo resistencia equivalente. Contenido de fibra de vidrio del 30%...
Conclusiones Clave El nailon con vidrio (PA66-GF) reemplaza al metal en HVAC con un ahorro de peso del 30–40% manteniendo resistencia equivalente. Un contenido de fibra de vidrio del 30% alcanza el punto óptimo: resistencia a la tracción 180–200 MPa, temperatura de deflexión por calor 220°C+. La ubicación de la línea de soldadura es el principal punto de falla — posiciona las entradas para alejar las líneas de soldadura de las zonas de tensión. En HVACore, utilizamos PA66-GF […]

Puntos Clave El nailon con carga de vidrio (PA66-GF) reemplaza al metal en HVAC con un ahorro de peso del 30–40% manteniendo resistencia equivalente. Contenido de fibra de vidrio del 30%...

Key Takeaways Glass-filled nylon (PA66-GF) replaces metal in HVAC at 30–40% weight savings with equivalent strength. 30% glass fiber content hits the sweet spot: tensile strength 180–200 MPa, heat deflection 220°C+. Weld line placement is the #1 failure point — position gates to push weld lines away from stress zones. At HVACore, we run PA66-GF […]
Read More
Read More
Piezas industriales de plástico y metal, incluyendo tapas y un perno sobre una superficie azul.
Puntos clave El grosor de la pared del jefe debe ser de 2.5x a 3.0x el diámetro exterior del inserto para evitar el agrietamiento por tensión circunferencial bajo ciclos repetidos de ensamblaje. Precalentar los insertos de latón a 80–100°C antes del moldeo reduce las fallas por agrietamiento por tensión retardada al eliminar el delta térmico de 200°C+ en la interfaz metal-plástico. Los patrones de moleteado en diamante proporcionan una retención de torque 30–40% mayor que los rectos […]

Piezas industriales de plástico y metal, incluyendo tapas y un perno sobre una superficie azul.

Key Takeaways Boss wall thickness must be 2.5x to 3.0x the insert outer diameter to prevent hoop stress cracking under repeated assembly cycles. Pre-heating brass inserts to 80–100°C before molding reduces delayed stress cracking failures by eliminating the 200°C+ thermal delta at the metal-plastic interface. Diamond knurl patterns provide 30–40% higher torque retention than straight […]